SCSC － TH abụrụla ihe ọhụrụ na-eguzogide iyi iji mepụta ihe mkpuchi nke hydrocyclones.
Àgwà nke ngwaahịa sintered silicon carbide gụnyere ike siri ike, ike dị elu na oke okpomọkụ. Agbanyeghị, ụdị ngwaahịa ndị a nwere ọghọm, dịka ike adịghị ike, adịghị ike na ihe ndị ọzọ. Iji mee ka ọ dabara na ọnọdụ ọrụ nke hydrocyclone, ọ dị mkpa ka emelite ya nke ọma. Zhongpeng emeela ka usoro ya ka mma, mepụta ma webata ihe ọhụrụ na-eguzogide iyi nke dabara adaba maka oke cyclone dị arọ nke a na-akpọ SCSC － TH. Ọ bụ ihe kristal ọhụrụ a na-emepụta site na ịgbakwunye ihe ndị na-egosi na usoro sintering silicon carbide ma na-eme ka ọ sie ike ma na-emeghachi omume na oke okpomọkụ. Isi ihe owuwu kemịkalụ ya bụ SiC, C, Mo, wdg. A na-emepụta nhazi hexagonal abụọ ma ọ bụ multivariate na gburugburu ebe okpomọkụ dị elu. Ya mere, ngwaahịa a nwere ike siri ike, ike dị elu, na-eme ka mmanụ na-amị amị (ala ala esemokwu), mgbochi nrapado, iguzogide nchara na oke okpomọkụ.
E gosiri ihe mejupụtara kemịkalụ na ihe ndị dị na ya na Tebụl 1 na Tebụl 2.
Tebụl 1: ihe mejupụtara kemịkalụ
| Mineral dị mkpa | Seramiki Silikọn Carbide | Nitrous oxide | Silicon efu |
| a － SiC | ≥98% | ≤0. 3% | ≤0. 5% |
Tebụl 2: njirimara anụ ahụ
| ihe | Carbide silicon a gbanyere agbawa na nrụgide ikuku | Silicon carbide mmeghachi omume graphite n'efu |
| Njupụta | 3. 1 g /cm3 | 3. 02 g /cm3 |
| Ntụpọsi | <0. 1% | <0. 1% |
| Ike ịgbagọ | 400 MPa | 280 MPa |
| modulus na-agbanwe agbanwe | 420 | 300 |
| Mgbochi asịd na alkali | Kachasị mma | Kachasị mma |
| Ike Vickers | 18 | 22 |
| Mmebi ahụ | ≤0. 15 | ≤0.01 |
N'otu ọnọdụ ahụ, atụnyere ihe ndị dị n'etiti seramiiki SCSC － TH na seramiiki alumina dị elu ka egosiri na Tebụl 3.
Tebụl 3: ntụnyere nke ihe onwunwe dị n'etiti SCSC － TH na Ai2O3
| ihe | Njupụta (g *cm3) | Nha ike nke Mons | Ike siri ike (kg*mm)2) | Ike ịgbagọ (MPa) | Mmebi ahụ |
| Ai2O3 | 3.6 | 7 | 2800 | 200 | ≤0. 15 |
| SCSC － TH | 3.02 | 9.3 | 3400 | 280 | ≤0.01 |
Ndụ ọrụ nke oké ifufe sistemụ etiti dị arọ na ọkpọkọ na-eguzogide iyi nke ejiri SCSC － TH mee bụ ugboro 3 ~ 5 nke Ai.2O3 na ihe karịrị okpukpu iri nke alloy na-eguzogide iyi. Ihe mkpuchi e ji SCSC － TH mee nwere ike ime ka mgbake nke coal dị ọcha dịkwuo elu karịa 1%. Ntụnyere ndụ ọrụ nke Ai.2O3 na SCSC － TH bụ dịka ndị a:
Tebụl 4: Nsonaazụ ntụnyere sitere na mmetụta nkewa nke oke ifufe dị n'etiti (%)
| ihe | Ọdịnaya < 1. 5 | Ọdịnaya 1.5~1. 8 | Ọdịnaya > 1.8 |
| Ai2O3 ihe mkpuchi | SCSC － TH liner | Ai2O3 ihe mkpuchi | SCSC － TH liner | Ai2O3 ihe mkpuchi | SCSC － TH liner |
| Kol dị ọcha | 93 | 94.5 | 7 | 5.5 | 0 | 0 |
| Ndị Middings | 15 | 11 | 73 | 77 | 12 | 8 |
| Nkume mkpofu | | | 1.9 | 1.1 | 98.1 | 98.9 |
Tebụl nke 5: Ntụnyere ndụ ọrụ nke Ai2O3 na SCSC
| | Ai2O3 Spigot | SCSC － TH Spigot |
| Ntụle na abrasion | 300 d | Mgbanwe 120 d | Abrasion na 1.5mm na ndụ ọrụ karịrị 3a |
| 500 d | Abrasion nke nwere 2mm na ndụ ọrụ karịrị 3a |
| Ọnụ ego mmezi | 300 d | 200,000 | 0 |
| 500 d | 300,000 | 0 |
Oge ozi: Maachị-12-2022